Fiberglass Multiaxial Fabric E Glass 


Description:

Multiaxial includes Uni-Directional, Biaxial, Triaxial, and Quadraxial Fabrics. The entire Partial warp. weft and double bias plies
are stitched into a single fabric. With our filament crimp in woven roving, the Multiaxial fabrics are the advantage of high strength, excellent stiffness, low weight, and thickness, as well as improved fabric surface quality. The fabrics can be combined with chopped strand mats or tissue or nonwoven materials.

Enquiry Now

Specification

Item Description
Uni-Directional Fabric ( 0° or 90°) The density of 0° Uni-Directional Fabric can be 300g/m²~900g/m² and density of 90° can be 150g/m²~1200g/m²
Biaxial Fabric (0°/90° or±45°) The density can be 300g/m²~2400g/m²
Triaxial Fabric

(0°/+45°/-45°) / (+45°/+90°/-45°)

The density can be 450g/m²~1800g/m²
Quadraxial Fabric

(0°/+45°/90°/-45°)

The density can be 600g/m²~2000g/m²

Product Application

Hand lay-up, filament winding, pultrusion, continuous laminating as well as closed molds.
Typical applications are found in boat building, transportation, anticorrosion, plane and automotive parts, furniture, and sports facilities.

Workshop

Storage

Pallet Packaging

Pacaked in woven boxes/bags

Pallet size:960×1300

Package

Woven Roving products must be stored in a cool, dry area. The recommended temperature is between 10 and 35 °C, and the relative humidity is between 35 and 75 %. If the product is stored at a low temperature (below 15 °C), it is recommended to condition the material in a workshop at least 24 hours before use.

Note

If the storage temperature is less than 15°C, it would be advisable to put the pallets in the processing area for 24 hours before use. This is to avoid condensation. It is recommended that products be consumed using a first-in, first-out method within 12 months of delivery.